Properties
|
Standards
|
Range
|
Result
|
Accreditations From
|
|---|---|---|---|---|
|
Flexural Modulus of Elasticity
|
BS EN ISO 178:2013
|
|
3070 N/mm2
|
SK Z-Germany & BSI-UK
|
|
Tensile Impact Strength
|
BS EN ISO 8256:2005
|
Not less than 600 KJ/m2
|
934 KJ/m2
|
SK Z-Germany & BSI-UK
|
|
Accelerated Weathering [25000 Hours @ 50 GJ/m2]
|
DIN EN 513
|
ΔE not more than 5
|
1.6
|
SK Z-Germany & BSI-UK
|
|
Charpy Impact Strength
|
BS EN ISO 179 -2:1999
|
Not less than 20 KJ/m2
|
74.4 KJ/m2
|
SK Z-Germany & BSI-UK
|
|
Reduction in Charpy Impact Strength
[Before & After Weathering]
|
DIN EN ISO 179 -1/1fA
|
Not More than 40%
|
10.4 %
|
SK Z-Germany
|
|
Vicat Softening Temperature
|
BS EN ISO 306:1997
|
Not less than 75oC
|
80oC
|
SK Z-Germany & BSI-UK
|
|
Heat Reversion @ 100o C, 60 Minutes
|
BS EN 12608-1:2016
|
To comply as per EN 12608-1:2016
|
Pass
|
BSI-UK
|
|
Resistance to Impact of Main Profile by falling Mass @-10oC,
|
BS EN 12608-1:2016
|
To comply as per EN 12608-1:2016
|
Pass
|
BSI-UK
|
|
Weld Strength (Individual Specimen)
|
BS EN 514:2000
|
|||
|
Heat Aging @ 150oC,30 Minutes,
|
To comply as per EN 12608-1:2016
|
Pass
|
BSI-UK
|
|
|
RoHS
|
DIRECTIVE 2011/65/EU
|
Lead should not be detected
|
Not detected
|
SGS
|
|
Flammability
|
UL-94
|
10 Sec
|
Vo
|
CIPET
|
|
Limiting Oxygen Index (LOI)
|
ASTM D2863
|
45%
|
47%
|
CIPET
|
|
Density
|
ASTM D 792
|
1.46 gm/cc
|
CIPET
|
|
|
Thermal Conductivity
|
ASTM E-1530
|
0.12 to 0.25 W/mk
|
0.137 W/mk
|
CIPET
|
|
Co-efficient of Linear Thermal Expansion
|
ASTM D 696
|